BSI 213 Epoxy 30 min 13 combined oz Yellow Package
"Why do I need epoxy?" One primary reason is price. Epoxy costs are about one fourth that of CA. When large objects are being bonded, economics can be a deciding factor on choice of adhesive. The specific characteristics of epoxies also give them advantages in some applications. All our epoxies are mixed with a 50-50 ratio. Any scrap material or paper scratch pad can be used as a mixing surface. We have found, however, that the plastic tops to coffee cans work best due to their outer border and their flexibility, which allows the unused cured epoxy to be released and thrown away.
Squeeze out equal length beads of the desired amount of epoxy, then mix together thoroughly with a popsicle stick or scrap piece of material. In cold weather, epoxy takes longer to cure (too cold and usually they never fully cure) and becomes more difficult to get out of the bottle, especially if it’s less than 1/2 full. The epoxies can be heated in a microwave oven for about 10 seconds so that they flow easier. The heating process, with the caps off, also releases any moisture that can be absorbed by epoxies. Their shelf life, therefore, is virtually unlimited.
Acetone works as the best solvent for cleaning epoxy from brushes and unwanted surfaces before it cures. If epoxy gets on surfaces that acetone will attack, use isopropyl alcohol. We do not recommend any additives for thinning epoxies due to their effect on curing and overall strength. If thin epoxy is required, either use heat or switch to EX-SLOW™ or FINISH-CURE™. Epoxies bond best to clean, textured surfaces. Smooth, non-porous surfaces should be roughened with coarse sandpaper to improve adhesion.
A small amount of CA can be used in strategic locations to hold parts in place while the epoxies cure. The minute designations for epoxies refer to the working time, i.e., the time one has before the epoxies begin to set up after being mixed in a large mass. When spread into thinner layers, the working time in increased significantly (except QUIK-CURE™). Working time decreases approximately 25% at temperatures above 90 degrees F. Don’t panic if your skin comes in contact with either epoxy or CA.
While contact should be avoided, uncured epoxy can be washed from your skin with soap and water. Allergic reactions are rare. Cured epoxy and CA can be peeled off the skin and usually are gone after a full day of normal activity. UN-CURE™ will debond any body parts that get stuck together if a peeling action (never pulling) doesn’t part them.
SLOW-CURE™ 30 min. epoxy works best for forming reinforcing fillets on joints. It has the highest strength of our epoxies. It is waterproof and more heat resistant. SLOW-CURE™ can be used for bonding if you’re willing to wait overnight. Fillers such as microballoons can be mixed with SLOW-CURE™ and FINISH-CURE™ to form a putty-like consistency. Such fillers will usually decrease the working time by about 25%. Bonded objects can be handled after 8 hours and the cured epoxy reaches full strength within 24 hours.
-
BSI 30 minutes
More like 15 minutes. There needs to be more thorough instructions on what conditions are needed to get 30 minutes of working time, especially if you need a large batch. Once applied, the glue works very well. I just don't like the idea that I wasted 2-half bottles of glue. I got feedback from BSI, however information UP FRONT, is what I needed.